Detailed Explanation of the Batch Foam Machine Foaming Process

The production of block-shaped soft foam typically utilizes the batch foam machine foaming process, a gap-type production method. This method evolved from manual foaming in laboratories. The process involves immediately pouring the mixed reaction materials into an open mold resembling a wooden or metal box, hence the name "boxed foam." The molds (boxes) for boxed foam can be rectangular or cylindrical. To prevent the foam block from forming a domed top, a floating cover plate can be placed on the top of the foam during foaming. The cover plate stays closely attached to the top of the foam and gradually moves upward as the foam rises.

The main equipment for boxed foam production includes: 1) Electric-mechanical stirrer, mixing barrel; 2) Mold box; 3) Weighing tools such as scales, platform scales, measuring cups, glass syringes, and other measuring devices; 4) Stopwatch for controlling mixing time. A small amount of mold release agent is applied to the inner walls of the box to facilitate easy removal of the foam.

The advantages of producing soft foam using the boxed foam method include: low equipment investment, small footprint, simple equipment structure, easy and convenient operation and maintenance, and flexible production. Some small and underfunded domestic and township enterprises use this method to produce polyurethane soft foam. Boxed foam molding is a non-continuous production method for soft foam, so the production efficiency is lower than continuous methods, and the equipment is mostly manually operated, resulting in higher labor intensity. Production capacity is limited, and there is a greater loss in cutting foam plastics. The process parameters for boxed foam should be controlled within a certain range because even with the same formula, the foam properties may not be the same when different process parameters are used. The raw material temperature should be controlled at (25±3) degrees Celsius, mixing speed at 900 to 1000r/min, and mixing time at 5 to 12 seconds. The mixing time of the polyether and additives mixture before adding TDI can be flexibly adjusted depending on the situation, and after adding TDI, a mixing time of 3 to 5 seconds is sufficient, with the key being thorough mixing after TDI addition.

During boxed foam molding, attention should be paid to the following aspects:

1) Prepare before production, including material temperature and machine equipment inspection;

2) Measure as accurately as possible;

3) Control the mixing time appropriately;

4) Pour the mixed material liquid quickly and steadily, avoiding excessive force;

5) Ensure the box is placed steadily, with the bottom paper flat, to avoid uneven material flow during pouring;

6) When the foam rises, gently press the cover to ensure the foam rises smoothly;

7) Additives should be used as specified, and pre-mixed materials should not be left for too long.

Three types of foam equipment have emerged in boxed foam molding. Initially, various raw materials were weighed into a container according to the formula, mixed with a high-speed mixer, and poured into the box mold for foaming and shaping. This method often resulted in residue in the mixing container. An improved method used a metering pump to transport the raw materials to the mixing barrel for uniform mixing. A mechanical device automatically closed the bottom of the barrel, and compressed air was used to press the material into the foaming box for shaping. Both of these methods could create eddies due to the rapid influx of materials into the box, which might cause defects or depressions in the foam products. The most reasonable boxed foam device is to place a bottomless mixing barrel directly in the center of the foaming box. A metering pump delivers the various raw materials needed for foaming into the mixing barrel. After mixing for a few seconds, the lifting device raises the mixing barrel out of the foaming box, allowing the foaming material to flow smoothly over the entire box bottom. This prevents foam cracking due to material eddies, and ensures relatively uniform height throughout the foam.

A pressure device can be added to the expanding foam material to produce flat-topped foam, reducing waste during cutting. This device is suitable for the production of polyether-type polyurethane soft foam and high rebound soft block foam. For polyvinyl acetate polyurethane blocks, this method cannot be used due to the high viscosity of the material, and continuous methods are generally employed.