Continuous Foaming Machine Related Calculations and Foaming Daily Operation

Calculation of foaming distance for continuous foaming machine

Given: Bubble release time for the formula is 108 seconds, conveyor belt speed during foaming is 4.6 meters per minute. Calculate the swinging and trough foaming distances.

Foaming distance when swinging: (108/60) x 4.6 = 8.28 meters

Foaming distance when troughing: [((108-18)/60)] x 4.6 = 6.9 meters

Explanation: For the same formula, continuous foaming machine has a shorter bubble release time than small bubbles. The calculated foaming distance is shorter than the actual foaming distance. This method only provides approximate confirmation of the foaming distance, supporting the adjustment of the settling plate. Troughing: 18" indicates the time in seconds that the raw material stays in the overflow trough.

Calculation of foaming height for continuous foaming machine

Given: Formula flow rate: 80 kilograms per minute for polyether, 20 for white polyether, 60 for TDI, 20 for stone powder, conveyor belt speed 4.5 meters per minute, mold width 1.65 meters, producing foam with a density of 25 kilograms per cubic meter. What is the foaming height in meters?

Total formula weight: 80 + 20 + 60 + 20 = 180 kilograms

Formula volume: 180/25 = 7.2 cubic meters

Base area of conveyor running per minute:

4.5 x 1.65 = 7.425 cubic meters

Foaming height: 7.2/7.425 = 0.97 meters

Explanation: Silicone oil, amine, and tin are not considered here as they offset the amount of carbon dioxide used during the foaming process. Moisture content (MC) is not considered because MC does not increase foam weight when vaporized.

Foaming Daily Operation

Beginners worry that improper adjustment of the settling plate will cause the liquid sprayed from the nozzle to surge forward or backward, affecting foaming. The reaction rate gradually increases within the first two minutes after starting the machine, sometimes requiring corresponding adjustments to the settling plate. Adjustments to the settling plate are more critical in formulas with low density and high MC.

TDI flow rate can be calculated by determining the corresponding scale value for the flow rate, but it is recommended to measure the TDI flow rate during the first foam production. Flow rate is too important; if the flow rate is incorrect, everything else will be a mess. It's best to rely on the simplest and most intuitive method of measuring flow rate.

When powder is being mixed, the mixed stone powder should be left overnight and production should start the next day. For formulations containing melamine and stone powder, it is recommended to first mix the melamine with the polyether for a period of time before adding the stone powder.

Formulas for foam machines with longer mixing chamber or more teeth on the mixing shaft typically have less amine and lower material temperature. Conversely, formulas for foam machines with shorter mixing chamber or fewer teeth on the mixing shaft typically have more amine and higher material temperature.

For the same formula, when switching between dual spray swing heads and single spray swing heads, if the cross-sectional area of the two nozzles is similar, the requirements for the fineness and number of layers of the mesh are similar.

Correction of small material flow rate can be done by measuring the return flow rate of the small material, or by dividing the total usage by the foaming time for correction. When the values obtained from the two correction methods differ significantly, the data from the second correction method should be used.

Formulas for soft foam with better properties are usually in an unstable range, such as lower TDI index, lower water to MC ratio, lower T-9 dosage, and lower silicone oil dosage. Just like in our jobs, there must be effort before reward.